AISI 3415 AMS6260E 655H13 15NiCr13 1.5752 Case Hardening Steel

AISI3415 AMS6260E 655H13 15NiCr13 1.5752 Case Hardening Steel

AISI3415 AMS6260E 655H13 15NiCr13 1.5752 Case Hardening Steel

1. 15NiCr13 Description

15NiCr13 is a remelted nickel chrome molybdenum case hardening steel produced by the PESR* (Pressurised ESR) method designed for components with high demand in toughness and core strength. 15NiCr13 is a remelted nickel chrome molybdenum case hardening steel designed for components with high demand in toughness and core strength. Compared with 15Cr and 15Cr steel, 15NiCr13 has high strength, plasticity, and hardenability. 15NiCr13 is mainly used to make high load under heavy load conditions.

Back to Top

2. 15NiCr13 Application

Highly stressed components in automotive construction, and for general engineering purposes, e. g. gears, crankshafts, gearshafts.

It is characterized by high strength and at the same time high plasticity of the core due to the high content of nickel in the chemical composition. Used, among others, as a steel for aviation, it is dedicated for use in parts of aircraft engines and for components of aviation equipment.

Equally often used for responsible parts of machinery and structures working with variable loads requiring abrasion resistance. 15NiCr13 grade is used as steel for gears and for control shafts, adjusting screws, axles, and rollers.

Back to Top

3.Advantages

Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.

Back to Top

4.All Grades Comparison

DIN EN ANFOR BS GOST AISI AMS UNI
1.5752 15NiCr13 14NC11 655H13 G55M13 3415 6260E 18NC13
Back to Top

5.Quality Standard

BS EN 10084 2008 Case hardening steels – Technical delivery conditions
BS EN 10277-4-2008 Bright steel products —Case Hardening Steel— Part 4 General

Back to Top

6. 15NiCr13 Chemical Composition(%)

C Mn Si P S Cr Ni
0.14-0.20 0.40-0.70 0.40 max 0.025 max 0.035 max 0.60-0.90 3.00-3.50
Back to Top

7.Mechanical Properties(T=20°C if not differently stated)

Process Diameter(mm) Tensile Strength Rm (Mpa) Yield Strength Rp0.2 (Mpa) Elongation A5 (%) Area Reduction Ratio C (%) Hardness (HB)
SOFT ANNEALED / / / / / 255 max
Treated to hardness range / / / / / 179-229
Treated to ferrite-pearlite structure / / / / 166-217
QUENCHED AND TEMPERED 11 max 1030–1320 835 min 9 min 40 min /
QUENCHED AND TEMPERED 11-30 930–1230 785 min 10 min 45 min /
QUENCHED AND TEMPERED 30-63 880–1180 735 min 10 min 45 min /
Back to Top

8.HEAT TREATMENT:

Process Temperature(oC)
End quench test Austenitizing 880 min
Carburizing 880-980
Core-hardening 840-880
Case-hardening 780-820
Tempering 150-200 /
Back to Top

9.Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.

Back to Top

In the grade of 12HN3A we supply:

  • round and flat hotrolled bars 12HN3A,15NiCr13,1.5752
  • forgings, forged bars, rings 12HN3A, 15NiCr13, 1.5752

Other replacements and equivalents

12CHN3A, 12KHN3A, 12XН3А, 12HN3A-SZ, 12HN3A-SH, 12CHN3A-SH, 12KHN3A-SH, 12XH3A-Ш, 15NICR13, 15 NICR 13, 1.5752, 5752, 14 NC 11, 14NC11, 14 NC 12, 14NC12, 16NC11, 16 NC 11, 16 NICR 11, 16NICR11, 14NI9, 14 NI 9, 14NICR14, 14 NICR 14, 1.5752, 5752, 12NC12, 12 NC 12, NCAV, FE-PL61, 14 NICR 10, 14NICR10, 12CRNI3A, 12 CRNI 3, 12 CRNI 3 A, A42123, BNC2, BNC 2, MSZ 31, SNC815, SNC 815, SNC22, SNC 22, 3415, J1249