Inconel Incoloy 901 N90901 2.4662 Alloy

 

Inconel 901 Alloy

Inconel 901 Alloy

With over 35 years of industry expertise, Fushun has the industry knowledge and resources to find you the metal products that you need for your specific industry applications. We are in stock and ready to quickly deliver hard-to-find metals. Our ISO 9001-certified metal supply is one of the most comprehensive selections on the market. We provide timely customer support and quick delivery on all quantities of our in stock products.

 

Contact us for more information regarding our nickel alloy manufacturing and distribution options.  Fushun is your trusted nickel alloy supplier for all types of Nickel alloy material.

 

Inconel incoloy 901 Alloy Description

Inconel 901 Alloy nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A substantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.

 

Inconel incoloy 901 Alloy APPLICATIONS

The alloy is used for components in aircraft and gas turbines, such as turbine rotors, compressor discs, hubs and shafts, with a maximum service temperature around 1100ºF (595ºC).

 

Inconel incoloy 901 Alloy Common Trade Names:

Inconel® 901, NIMONIC® 901, Alloy 901, AISI 681, AISI 682, PWA 1002, PWA 1003, SPS M259, UNS N90901, AMS 5660, AMS 5661, B50A305B, Werkstoff 2.4662, DIN 1.4898,

 

Inconel incoloy 901 Alloy Specifications:

bar AMS 5661/AMS 5660 Dia. 1-500mm
forging/ring AMS 5661 As Request
wire AMS 5830 Dia. 0.1-30mm

Inconel incoloy 901 Alloy Chemical Composition

The chemical composition of Inconel 901 ™ is outlined in the following table.

Element Content (%)
Nickel, Ni 41-43 .5
Chromium, Cr 11-14
Titanium, Ti 2.2-2.75
Silicon, Si 1 max
Manganese, Mn 0.8 max
Copper, Cu 0.5 max
Aluminum, Al 0.35 max
Carbon, C 0.1 max
Phosphorus, P 0.04 max
Sulfur, S 0.04 max
Boron, B 0.01 – 0.02
Iron, Fe Remainder

Inconel incoloy 901 Alloy Corrosion Resistance

Alloy 901 has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.

 

Inconel incoloy 901 Alloy FORGING

The alloy is forged between 2050/1850ºF (1120/1010ºC). Some light reductions may be carried out down to 1600ºF (870ºC) but not below. For rapid forging the metal temperature should not exceed 2050ºF (1120ºC).

 

Inconel incoloy 901 Alloy Heat Treatment

  1. Solution Treatment: 1975/2025°F (1080/1107°C), hold 2 hours at heat, and water quench.
  2. Stabiliztion Treatment: 1400/1475°F (760/802°C), hold 2 to 4 hrs, and air cool.
  3. Precipitation Hardening Treatment:1300/1375°F (704/746°C), hold for 24 hours, and air cool.

 

Mechanical Properties of Inconel incoloy 901 Alloy

901 bar is to ordered to AMS 5660 is supplied either solution annealed or solution annealed and aged, and may be machined in either condition.  Good results are often obtained by rough machining in the solution annealed condition and finishing after heat treatment.  Carbide tooling generally produces the highest cutting rates and is recommended for most turning operations involving uninterrupted cuts.  High speed steel tools may be used for interrupted cuts, finishing to close tolerances and cutting with the least amount of cold work hardening.  Care must be taken to ensure that a positive cutting action is achieved at all times, otherwise glazing (work hardening) will occur which will inhibit further machining.

 

Inconel incoloy 901 Alloy Tensile Properties

Solution Treated: 2000°F (1093°C), 2 hours, water quenched. Stabilized: 1425°F (774°C), 4 hours , air cooled. Aged: 1350°F (732°C), 24 hours, air cooled.

Test
Temperature
0.2% Offset
Yield Strength
Ultimate
Tensile Strength
% Elongation
in 2″
% Reduction
of Area
°F °C ksi MPa ksi MPa
70
800
1000
1200
1300
1400
1500
21.1
427
538
649
704
760
816
125.0
116.5
113
117
114
102.5
79
862
803
779
807
786
707
545
175
159
156
150
130
107.5
81
1207
1096
1076
1034
896
741
559
15.0
16.0
17.0
14.0
11.5
9.0
13.0
19.0
25.5
29.0
21.0
15.5
14.5
20.0

 

Inconel incoloy 901 Alloy Stress Rupture Strength

Solution Treated: 2000°F (1093°C), 2 hours, water quenched. Stabilized: 1425°F (774°C), 4 hours , air cooled. Aged: 1350°F (732°C), 24 hours, air cooled.

Test
Temperature
Stress to Produce Rupture in
°F °C 10 Hours 100 Hours 1000 Hours
ksi MPa ksi MPa ksi MPa
1000
1200
1350
1500
538
649
732
816

96.5
60
35

665
414
241
120
90
51
22.5
827
621
352
155
100
75
33
11
689
517
228
76

Inconel incoloy 901 Alloy Hot Working

Alloy 901 is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.

 

Inconel incoloy 901 Alloy Weldability

Alloy 901 can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.

Quality & Testing

Fushun supply Certification with all shipments, containing full chemical analysis and also mechanical test results if requested.

 

All incoming material is visually inspected and PMI (Positive Material Identification) tested before processing begins and all our production material is checked during each stage of processing.

 

All incoming orders are produced to the individual customer specification, some of which may involve processing sample batches for testing prior to full production.

 

Final Inspection carried out on all finished material to include:

Visual inspection

Dimensional checks

PMI (Positive Material Identification)

Mechanical tests

 

Nickel Alloy Material Available Formats

Fushun offers pure Nickel alloy materials in a variety of forms, including:

Seamless & welded pipe

Seamless & welded tube

Bar

Wire

Sheet

Plate

Forgings

Pipe fittings

Flanges

Weld Rod

 

Nickel Alloy Supply Quantities for Single Items or Full Bills

At Fushun, we can supply single items or full bills of nickel alloy materials for most any project. No inquiry is too small. We offer quick responses to customer inquiries and specialize in the rapid delivery of both large and small quantities of nickel alloy products.

 