1.2379 D2 SKD10 Tool Steel Vacuum Hardened Machined Block

price:
Contact customer service
Heat Treatment
Cold Processing
Hot Working

1.2379 D2 SKD10 Tool Steel Vacuum Hardened Machined Block

1.2379 D2 SKD10 Tool Steel Vacuum Hardened Machined Block

1.2379 D2 SKD10 Tool Steel Vacuum Hardened Machined Block

D2 Tool Steel Introduction:

D2 steel is a high carbon – high chromium air hardening tool steel, heat treatable to 60-62 HRC. D2 offers excellent wear and abrasion resistance, due to large volumes of carbides in the micro-structure. D2 steel is widely used in long production cold work applications requiring very high wear resistance and high compression strength. It is machinable in the annealed condition, and, like other air hardening tool steels, exhibits minimal distortion in heat treat. D2 steel is available in de-carb free rounds, flats, and squares, as well as ground flat stock and drill rod.

 

D2 Tool Steel Applications:

Typical applications for D2 steel are blanking, forming, and trim dies, gages, slitting cutters, wear parts, lamination dies, thread rolling dies, drawing dies, rotary cutting dies, knurls, bending dies, gages, shear blades, burnishing tools, rolls, machine parts, master parts, injection screw and tip components, seaming rolls, extrusion dies, tire shredders, scrap choppers, Stamping dies, Forming Dies, Punches, Forming Rolls, Knives, slitters, shear blades, Tools, Scrap choppers, Tyre shredders, etc.

 

D2 Tool Steel All Grades Comparison:

ASTM Material No. DIN EN JIS
D2 1.2379 X155CrVMo12-1 X160CrMoV121 SKD10

 

D2 Tool Steel Chemical Composition(%)

C Si Mn P S Cr Mo V
1.40-1.60 0.10-0.60 0.10-0.60 0.030 max 0.030 max 11.0-13.0 0.70-1.20 0.50-1.10

 

D2 Tool Steel Quality Standard:

ASTM A681 – 08 Standard Specification for Tool Steels Alloy.

 

D2 Tool Steel Size and Tolerance

Products Data(Unit mm)
Products Width Width Tolerance Thickness Tolerance Straightness Perpendicularity Flatness Parallelism Plate Surface Roughness Plate Side Roughness
Precision Plate <600 0 to +0.1 0 to +0.1 0.02/100 0. 01/100 0. 01/100 0. 02/100 Ra <1.6 or Rz<6.3 Ra<3. 2 or Rz<12.5
600-1000 0 to +0.15 0 to +0.1
1000-2000 0 to +0. 2 0 to +0.15
Polished Plate <600 0 to +0. 5 0 to +0.5 0. 06/100 0. 05/100 Ra<1.6 or Rz<6.3 Ra<6. 3 or Rz<25
>600 0 to +1
Polished Plate for Heat-treat <600 +0.3 to +0.8 +0. 3 to +0.6 0. 06/100 0. 05/100 Ra<3.2 or Rz<12.5
>600 0 to +1
Grounded Plate <600 -1 to +1 -2 to 0 / 0. 05/100 Ra<3. 2 or Rz<12.5 Ra<6. 3 or Rz<25
>600 -1 to +1 -3 to 0
Other size or requirement please send to info@fushunspecialsteel.com

 

D2 Tool Steel Heat-Treatment Option

1 Annealed: Heat slowly to 1550°-1600°F, hold until entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which cooling rate may be increased.

2 Vacuum heat treatment : Quenched and Tempered:

Type Preheat Temperature,°F (°C) Salt Bath Controlled Atmosphere Furnaces Austenitizing Time (minutes) Quench Medium Tempering Temperature,°F (°C) Minimum Hardness,RC
D2 1500 (816) 1825 (996) 1850 (1010) 10-20 Air 400 (204) 59

 

D2 Tool Steel Surface Option

hot rolled, forged, blasted or pickled, cold drawn, machined, ground, precision ground and polished

 

D2 Tool Steel Smelting Option

1 EAF+VLF: Electric Arc Furnace +Vacuum Ladle Furnace

2 EAF+ESR: Electric Arc Furnace + Electro Slag Remelting

 

D2 Tool Steel Delivery Option

Package: Plastic material bundled ; wooden case ; wooden/steel pallet ; client’s requirement

Payment: Paypal / TT

Transport: DHL / FEDEX / UPS / EMS

 

D2 Tool Steel Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.