1.2419 105CrW6 DIN SKS31 O7 Cold Working Die Steel
1.2419 105CrW6 DIN SKS31 O7 Cold Working Die Steel
1 1.2419 Introduction:
O7 Cold Working Die Steel is one kinds of oil hardening cold working die steel, which consists of chromium and manganese, and has higher tungsten content than grade O1. The O7 steel has the best wear resistance among the O series steels, however, it has relatively low hardenability.
Back to Top
2 1.2419 Applications:
Cutting and punching tools for sheet thickness up to 6 mm, also for paper and plastics, roll shear blades for sheet thickness up to 6 mm, small bending and drawing tools, thread cutting tools, reamers, woodworking tools, gauges and other measuring tools, small inserts and plastic moulds.
Back to Top
3 Quality Standard:
ASTM A681 – 08 Standard Specification for Tool Steels Alloy.
BS EN ISO 4957 Tool Steel
JIS G4404 Alloy Tool Steel
Back to Top
4 All Grades Comparison:
Back to Top
5 Chemical Composition(%)
| Steel Grade | C | Si | Mn | P | S | Cr | V | W | Mo |
|---|---|---|---|---|---|---|---|---|---|
| O7 | 1.10-1.30 | 0.10-0.60 | 0.20-1.00 | 0.030 max | 0.030 max | 0.35-0.85 | 0.15-0.40 | 1.00-2.00 | 0.30 max |
| SKS31 | 0.95-1.05 | 0.35 max | 0.90-1.20 | 0.030 max | 0.030 max | 0.80-1.20 | / | 1.00-1.50 | / |
| 105WCr6 | 1.00-1.10 | 0.1-0.40 | 0.80-1.10 | 0.030 max | 0.030 max | 0.90-1.10 | / | 1.00-1.30 | / |
| CrWMn | 0.90-1.05 | 0.40 max | 0.80-1.10 | 0.030 max | 0.030 max | 0.90-1.20 | / | 1.20-1.60 | / |
Back to Top
6 HEAT TREATMENT:
- FORGING: Hot forming temperature: 1050-850oC SOFT ANNEALING: Heat to 720-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230. STRESS RELIEVING:Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment. HARDENING:Harden from a temperature of 800-830oC followed by oil quenching or warm bath quenching approx. 200oC. Hardness after quenching is 63-65 HRC. TEMPERING: Tempering temperature: See the data bellow.
| Tempering Temperature | Hardness(HRC) |
|---|---|
| 100oC | 64 |
| 200oC | 61 |
| 300oC | 58 |
| 400oC | 54 |
| 500oC | 49 |
| 600oC | 41 |
| 650oC | 30 |
Back to Top
7 1.2419 Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.