GRADE 310S STAINLESS STEEL


310S is an AOD melted austenitic stainless steel with high chromium and nickel content.  This alloy has excellent resistance to oxidation at high temperatures making it suitable for furnace rails and dunnage.  This grade is used often in carburizing atmospheres that are common in petrochemical industries.

 

SPECS USAP PRODUCES TO:

  • AMS 5651
  • AMS-QQ-S-763
  • ASTM A276
  • ASTM A479

 

INDUSTRY / TRADE NAMES

  • UNS S31008
  • UNS S31009
  • 4845

 

APPLICATIONS:

The higher alloyed stainless steels generally have excellent strength at elevated temperatures along with outstanding resistance to creep deformation and environmental attack. Therefore, stainless 310s is used widely in industries such as heat treatment and chemical processing. Some examples include:

  • Furnace Parts
  • Oil Burner Parts
  • Heat Exchangers
  • Welding Filler Wire and Electrodes
  • Annealing Covers
  • Combustion Tubes
  • Fire Box Sheets

 

Chemical Properties:

% Cr Ni C Si Mn P S Mo Cu Fe
310S min: 24.0
max:26.0
min: 19.0
max: 22.0
0.08 1.00 2.0 0.045 0.030 0.75 0.5 balance

Smelting Option

1 EAF: Electric Arc Furnace

2 EAF+LF+VD: Refined-smelting and vacuum degassing

3 EAF+ESR: Electro Slag Remelting

4 EAF+PESR: protective atmosphere Electro Slag Remelting

5 VIM+PESR: Vacuum induction melting

 

Forming Option

1 Hot rolling process

2 Hot Forging: Electro-hydraulic; High-speed-hydraulic; Oil-hydraulic; Precision-forging

 

Heat-treatment Option

1 +A: Annealed (full/soft/spheroidizing)

2 +N: Normalized

3 +NT: Normalized and tempered

4 +QT: Quenched and tempered (water/oil)

5 +AT: Solution annealed

6 +P: Precipitation hardened

Suface Option

1 Black Surface

2 Grounded: Bright but rough ; Not precision

3 Machining for plate: Bright and precision; Little turning scar

4 Peeled/Turned: Bright and precision; Little turning scar

5 Polished: Very Bright and precision size; Not turning scar

 

Other Services

1 Cutting: Small pieces

2 CNC Machine: Produce as your drawing

3 Package: Bare/Nylon/Canvas/Wooden

4 Payment:T/T, L/C, O/A(request credit)

5 Transport:FOB/CFR/CIF/DDU/DDP (train/ship/Air)

 

Mechanical Properties:

Grade Tensile Strength
ksi (min.)
Yield Strength 0.2%
Offset ksi (min.)
Elongation –
% in
50 mm (min.)
Hardness
(Brinell) MAX
Hardness
(Rockwell B) MAX
310S 75 30 40 217 95

 

CORROSION RESISTANCE:

  • Provides excellent corrosion resistance
  • High chromium content allows for good aqueous corrosion resistance
  • Excellent resistance at normal temperatures and also has good resistance to oxidizing and carburizing atmospheres

 

HEAT RESISTANCE:

  • Good resistance to oxidation in intermittent service in air at temperatures up to 1040°C and 1150°C in continuous service.
  • Good resistance to thermal fatigue and cyclic heating.
  • Widely used where sulphur dioxide gas is encountered at elevated temperatures.
  • Continuous use in 425-860°C range not recommended due to carbide precipitation, if subsequent aqueous corrosion resistance is needed
  • Generally used at temperatures starting from about 800 or 900°C – above the temperatures at which 304H and 321 are effective.

 

FABRICATION:

  • Commonly used in the heat treatment and process industries due to high temperature and corrosive environments
  • Often fabricated into complex structures
  • Roller-forms, stamps and draws readily
  • Because 310swork hardens, severe forming operations should be followed by an anneal

 

WELDABILITY:

  • Austenitic stainless steel is generally considered to be weldable
  • Generally considered to have weldability equivalent to 304 and 304L
  • Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion